Heat Shrink End Caps & End Caps with Valves
The ideal heat shrink temperature for the end caps is around 275F (135C). Applying the heat shrink end cap can be simple and hassle-free.
|
|
Heat Shrink End Caps & End Caps with Valves
|
|
|
|
|
|
Variations
| Part Number |
Size (inches) |
ID (before shrinking) (inches) |
ID (after shrinking) (inches) |
| HSEC-0375 |
3/8 |
0.39 |
0.16 |
| HSEC-050 |
1/2 |
0.55 |
0.18 |
| HSEC-075 |
3/4 |
0.75 |
0.25 |
| HSEC-100 |
1 |
1 |
0.31 |
| HSEC-100-V |
1 w/ Valve |
1 |
0.31 |
| HSEC-150 |
1-1/2 |
1.38 |
0.59 |
| HSEC-150-V |
1.5 w/ Valve |
1.38 |
0.59 |
| HSEC-200 |
2 |
2.17 |
1 |
| HSEC-200-V |
2 w/ Valve |
2.17 |
1 |
| HSEC-300 |
3 |
2.95 |
1.38 |
| HSEC-300-V |
3 w/ Valve |
2.95 |
1.38 |
| HSEC-400 |
4 |
3.94 |
1.97 |
| HSEC-400-V |
4 w/ Valve |
3.94 |
1.97 |
| HSEC-500 |
5 |
4.72 |
2.36 |
| HSEC-500-V |
5 w/ Valve |
4.72 |
2.36 |
Features and Benefits
- The End Cap is adhesive lined to bond with the heat shrink it overlaps
- Hot melt adhesive seals and insulates in one step to speed installation
- Adhesive lining will prevent moisture penetration, allowing for long term storage of cable
- Forms pressure-tight seal on ends of communication and power cables
- Shrink ratio of 3:1 insulates a wide range of diameters and irregular shapes
- Cross-linked UV resistant material improves chemical and temperature resistance
- 3 to 1 shrink ratio, so only 6 sizes are needed to cover a range of 0.16" to 5"
- Continuous use temperature of up to 110 °C
- Shrink temperature of 120-135 °C
- Dual wall end cap, with internal wall of hot-melt adhesive provides excellent bonding to plastic and metals.
- Capable of sealing the entire surface of a cable or wire
Specifications
| Nominal Size (inches) |
ID (before shrinking) (inches) |
ID (after shrinking) (inches) |
Wall (after shrinking) (inches) |
Length (before shrinking) (inches) |
| 3/8 |
0.39 |
0.16 |
0.08 |
1.34 |
| 1/2 |
0.55 |
0.18 |
0.08 |
1.77 |
| 1 |
1 |
0.31 |
0.09 |
2.76 |
| 1-1/2/td>
| 1.38 |
0.59 |
0.12 |
3.35 |
| 2 |
2.17 |
1 |
0.13 |
4.33 |
| 3 |
2.95 |
1.38 |
0.14 |
5.12 |
| 4 |
3.94 |
1.97 |
0.16 |
6.1 |
| 5 |
4.72 |
2.36 |
0.16 |
6.1 |
More Information
| ORDER REF. NUMBER |
AS SUPPLIED (mm) |
After recovered (mm) |
|
|
|
Cable |
| Standard length end caps |
D (Min) |
D (Max.) |
A (10%) |
L(10%) |
Dw (5%) |
Diameter |
| 12/4 |
12 |
4 |
15 |
40 |
2.6 |
4 10 |
| 14/5 |
14 |
5 |
18 |
45 |
2.2 |
5 10 |
| 20/6 |
20 |
6 |
25 |
55 |
2.8 |
6 16 |
| 25/8.5 |
25 |
8.5 |
30 |
68 |
2.8 |
10 20 |
| 35/16 |
35 |
16 |
35 |
83 |
3.3 |
18 32 |
| 55 / 26 |
55 |
26 |
50 |
103 |
3.5 |
28 48 |
| 75/36 |
75 |
36 |
55 |
120 |
4 |
45 68 |
| 100/52 |
100 |
52 |
70 |
140 |
4 |
55 90 |
| 120/60 |
120 |
60 |
70 |
150 |
4 |
65 110 |
| 145/60 |
145 |
60 |
70 |
150 |
4 |
70 130 |
| 160/82 |
160 |
82 |
70 |
150 |
4 |
90 150 |
| 200/90 |
200 |
90 |
70 |
160 |
4.2 |
100 180 |
Technical Data :
| PROPERTY |
TEST METHOD |
VALUE |
| Operating temperature |
IEC 216 |
-55 ℃ to +110 ℃ |
| Tensile strength(psi) |
ASTM D638 |
> 14 MPa |
| Elongation at break (%) |
ASTM D638 |
> 400% |
| Density |
ASTM D792 |
1.05 |
| Elongation at break after aging |
150 / 168hrs |
> 300% |
| Dielectrict strength |
IEC 243 |
> 15kV / mm |
| Volume resistance |
IEC 93 |
> 10 Ω.cm |
|
| |